dc.contributor.advisorConde Rivera, Laura Rosa
dc.contributor.advisorLópez Suarez, Franz Edwin
dc.coverage.spatialBogotá, Colombiaspa
dc.creatorRamírez Valencia, Lilian Daniela
dc.date.accessioned2018-08-22T22:35:40Z
dc.date.available2018-08-22T22:35:40Z
dc.date.created2018
dc.identifier.urihttp://hdl.handle.net/20.500.12010/4276
dc.descriptionLas tecnologías de almacenamiento de energía como los supercapacitores electroquímicos, requieren el estudio de nuevos materiales de carbono que puedan ser usados como electrodos y permitan la obtención de una alta capacitancia; para ello, se requiere que el material carbonoso tenga una alta área específica, un alto desarrollo de porosidad y grupos funcionales de oxígeno en su superficie. En este trabajo se desarrolla un material carbonoso a partir de la cascarilla de cacao usando KOH como agente activante, se obtuvieron materiales a tres relaciones agente/sólido (1:1, 3:1 y 5:1 p/p), y tres temperaturas de carbonización (500, 650 y 800 °C), a fin de conocer las mejores condiciones de obtención. Los carbones activados obtenidos a partir de la cascarilla de cacao, se caracterizaron mediante análisis próximo e isotermas de adsorción de N2 y CO2; las muestras con mayor área superficial BET se caracterizaron además a través de espectroscopia Raman, descomposición con temperatura programada DTP, y espectroscopia fotoelectrónica de rayos-X XPS, con el fin de determinar la composición química y caracterizar la estructura de la superficie; el desempeño electroquímico de estas muestras se evaluó por voltarimetría cíclica (VC). La muestra sintetizada con una relación agente/Sólido de 5:1 y carbonizada a 650 oC (CC-650-5), fue la que presentó la mayor área superficial, 1443 m2/g, con la mayor capacitancia específica de 132 F/g; esta muestra presentó el menor contenido de cenizas, el mejor desarrollo de microporosidad, el menor desorden en su estructura y por lo tanto tuvo una alta conductividad eléctrica; además en su superficie se encontraron grupos funcionales oxigenados como los carbonilos, quinonas y fenoles, que pudieron favorecer el almacenamiento de energía.spa
dc.description.abstractEnergy storage technologies such as electrochemical supercapacitors, require the study of new carbon materials with high surface area, high development of porosity and functional oxygen groups on their surface, to be used as electrodes with high capacitances. In this work, carbon materials were developed from cocoa husk using KOH, at three agent/solid ratios (1:1, 3:1 y 5:1 p/p) and three carbonization temperatures (500, 650 y 800 °C), in order to know the best conditions. The activated carbons were characterized by proximate analysis, N2 and CO2 adsorption isotherms; the samples with higher BET surface areas were also analyzed by Raman spectroscopy, temperature programed decomposition (DTP), and X-ray photoelectron spectroscopy (XPS), in order to determine their chemical composition, and surface structure; the electrochemical performance of these samples were evaluated by cyclic voltammetry (CV). The sample obtained at an agent/solid ratio of 5:1 and at a temperature of 650 oC showed the highest surface area, 1443 m2/g, and the highest specific capacitance of 132 F/g, presenting the lowest ash content, better development of microporosity and less disorder in its structure increasing the electrical conductivity; additionally, oxygenated groups such as carbonyl, quinones and phenols were found on its surface, and could favored the storage of energy, increasing the capacitance.spa
dc.format.extent46 páginasspa
dc.format.mimetypeapplication/pdfspa
dc.language.isospaeng
dc.publisherUniversidad de Bogotá Jorge Tadeo Lozanospa
dc.sourcereponame:Expeditio Repositorio Institucional UJTLspa
dc.sourceinstname:Universidad de Bogotá Jorge Tadeo Lozanospa
dc.subjectSupercapacitorspa
dc.subjectElectrodosspa
dc.subjectCapacitanciaspa
dc.subjectDoble capaspa
dc.subjectPseudocapacidadspa
dc.subjectCascarilla de cacaospa
dc.titleObtención de materiales carbonosos a partir de la cascarilla de cacao para su aplicación como electrodos en supercapacitoresspa
dc.typeinfo:eu-repo/semantics/bachelorThesiseng
dc.type.spaTrabajo de gradospa
dc.subject.lembQuímica, Ingenieríaspa
dc.subject.lembQuímicaspa
dc.subject.lembSoluciones (Química)spa
dc.subject.lembCircuitos eléctricosspa
dc.subject.lembIndustrias electrónicasspa
dc.subject.lembAnálisis de circuitos eléctricosspa
dc.type.hasVersioninfo:eu-repo/semantics/acceptedVersionspa
dc.rights.accesoAbierto (Texto Completo)spa
dc.subject.keywordSupercapacitorspa
dc.subject.keywordElectrodespa
dc.subject.keywordCapacitancespa
dc.subject.keywordDouble layerspa
dc.subject.keywordPseudocapacityspa
dc.subject.keywordCocoa huskspa
dc.creator.degreeIngeniero(a) Químicospa
dc.publisher.programIngeniería Químicaspa
dc.publisher.departmentFacultad de ciencias naturales e ingenieríaspa


Files in this item

Thumbnail
Thumbnail

This item appears in the following Collection(s)

Show simple item record